Incorporated Cure Polymers
| product | Test cpd | %F | S.G | Mooney Viscosity (ML1+10 @121℃ ) | TR10 (℃ ) | Tensile (psi) | Elong (%) | M100 (psi) | Duro (Shore A pts) | Comp Set ASTM D395 Method B (70 hrs @200℃ ) | Comments |
|
O-Ring Applications ( see new FG grades for FDA applications) |
|||||||||||
| FE Products | |||||||||||
| FE-5610Q |
l
|
65.9 | 1.80 | 9 | -18 | 1930 | 210 | 800 | 75 | 21 |
These are cleanest running Dyneon O-ring grade polymers available. They
provide excellent mold release and improved scorch safety.
These properties allow molding at higher temperatures(>200℃/392。 F)for faster cure cycles while resulting in parts with improved dimensional stability. Can be compounded to meet Mil-R-83248 and others. See data sheets. FE-5621Q and FE-5641Q have lower mold shrinkage
|
| FE-5620Q |
l
|
65.9 | 1.80 | 23 | -18 | 2240 | 195 | 950 | 77 | 13 | |
| FE-5621Q |
l
|
65.9 | 1.80 | 23 | -18 | 2240 | 195 | 950 | 77 | 13 | |
| FE-5623Q |
l
|
65.9 | 1.80 | 23 | -18 | 2400 | 180 | 1060 | 79 | 13 | |
| FE-5640Q |
l
|
65.9 | 1.80 | 40 | -18 | 2370 | 200 | 1050 | 77 | 11 | |
| FE-5641Q |
l
|
65.9 | 1.80 | 40 | -18 | 2340 | 185 | 970 | 76 | 11 | |
| FE-5660Q |
l
|
65.9 | 1.80 | 60 | -18 | 2400 | 200 | 1150 | 77 | 9 | |
| FE-5840Q |
l
|
70.1 | 1.80 | 37 | -7 | 2000 | 210 | 980 | 84 | 26 | |
| Other Products | |||||||||||
| FC-2110Q |
l
|
65.9 | 1.80 | 9 | -18 | 2010 | 170 | 950 | 77 | 19 | Excellent processability. Viscosity modifier. Suggested alternative: FE -5610Q |
| FC-2121 |
l
|
65.9 | 1.80 | 23 | -18 | 2375 | 180 | 1025 | 77 | 14 | Excellent processability. Suggested alternative : FE-5620Q. |
| FC-2174 |
l
|
65.9 | 1.80 | 40 | -18 | 2450 | 180 | 1050 | 78 | 12 | Excellent processability. Suggested alternative : FE-5640Q. |
| FC-2179 |
l
|
65.9 | 1.80 | 80 | -18 | 2475 | 180 | 1100 | 76 | 10 | Excellent processability. Suggested alternative : FE-5660Q. |
| FC-2180 |
l
|
65.9 | 1.80 | 40 | -18 | 2370 | 180 | 1025 | 75 | 12 | Lower mold shrinkage and excellent compression set resistance. |
| Molded Goods Applications (see new FG grades for FDA applications) | |||||||||||
| FE Products | |||||||||||
| FE-5622Q |
l
|
65.9 | 1.80 | 22 | -18 | 2250 | 235 | 640 | 74 | 18 |
These are Dyneon's cleanest running molded goods polymers. thy provide improved improved flow, mold release and scorch safety. They offer improved meltal adhesion. Excellent for parts with complex profiles. Cleaner running than FX-9038 with improved release and compression set resistance. |
| FE-5642Q |
l
|
65.9 | 1.80 | 40 | -18 | 2312 | 220 | 690 | 72 | 17 | |
| FE-5840Q |
l
|
70.2 | 1.86 | 37 | -7 | 2000 | 210 | 980 | 84 | 26 | |
| Other Products | |||||||||||
| FC-2122 |
l
|
65.9 | 1.80 | 25 | -18 | 1900 | 310 | 520 | 75 | 25 | Good flow, release and hot tear for complex part. Suggested alternative : FE-5622Q |
| FC-2123 |
l
|
65.9 | 1.80 | 25 | -18 | 2350 | 270 | 530 | 71 | 20 | Excellent hot tear and compression set. Good metal adhesion . Suggested alternative : FE-5622Q |
| FC-2144 |
l
|
65.9 | 1.80 | 41 | -18 | 2540 | 260 | 550 | 70 | 17 | higher viscosity version of FC-2123. Suggested alternative : FE-5642Q |
| FC-2152 |
l
|
65.9 | 1.80 | 51 | -18 | 2100 | 305 | 550 | 73 | 22 | Improved hot tear over FC-2176. Suggested alternative : FE-5642Q |
| FC-2176 |
l
|
65.9 | 1.80 | 30 | -18 | 2175 | 240 | 600 | 71 | 22 | Good general purpose grade with good tear resistance and scorch safety. |
| FC-2177 |
l
|
65.9 | 1.80 | 33 | -18 | 1865 | 240 | 700 | 75 | 21 | Slower cure rate and high tear strength for bonded seals. |
| FC-2181 |
l
|
65.9 | 1.80 | 44 | -18 | 2560 | 240 | 690 | 72 | 13 | Combindes high elongation with excellent compression set resistance. Suggested alternative : FE-5642Q |
| FLS-2530 |
l
|
69.0 | 1.85 | 38 | -8 | 2200 | 255 | 700 | 77 | 19 | High fluorine dipolymer with improved fluid resistance over lower fluorine dipolymers. |
| Hose/Extrusion Applications | |||||||||||
| FE Products | |||||||||||
| FE-5730Q |
l
|
69.2 | 1.86 | 32 | -12 | 1460 | 330 | 375 | 71 | 45 | 69.2% F grade terpolymer with good permeation resistance to auto fluids. Gives smooth extrudates without process aids. Can be compounded to pass -40℃ mandral flex test. |
| FE-5830Q |
l
|
70.5 | 1.90 | 33 | -7 | 1600 | 250 | 640 | 80 | 44 | 70.5% F grade terpolymer with best permeation resistance to auto fluids. Gives smooth extrudates without process aids. Can be compounded to pass -40℃ mandral flex test. |
| Other Products | |||||||||||
| FC-2120 |
l
|
65.9 | 1.80 | 23 | -18 | 2140 | 200 | 850 | 75 | 16 | Dipolymer for diffcult extrusions. |
| FC-2182 |
l
|
65.9 | 1.80 | 30 | -18 | 2200 | 265 | 550 | 70 | 22 | Dipolymer for autoclave curning. |
| FC-2320 |
l
|
69.0 | 1.86 | 23 | -12 | 2000 | 230 | 750 | 79 | 39 | 69% F grade terpolymer for diffcult extrusions. Suggested alternative : FE-5730Q or FE-5830Q. |
| Fx-11818 |
l
|
68.6 | 1.80 | 28 | -14 | 1800 | 290 | 490 | 74 | 43 | 68.6% F grade terpolymer for diffcult extrusions. Suggested alternative : FE-5730Q or FE-5830Q. |
Incorporated Cure Polymers(Cont.)
| product | Test cpd | %F | S.G | Mooney Viscosity (ML1+10 @121℃ ) | TR10 (℃ ) | Tensile (psi) | Elong (%) | M100 (psi) | Duro (Shore A pts) | Comp Set ASTM D395 Method B (70 hrs @200℃ ) | Comments |
| Food Grade Applications | |||||||||||
| FG Products | |||||||||||
| FG-5630Q |
l
|
65.9 | 1.80 | 30 | -18 | 2140 | 210 | 810 | 77 | 13 | When compared to other food grade DiakTM cured compounds, these products offer improved mixed compound shelf-life, mold flow and release, as well as better water and compression set resistance. These are O-ring grades that can be diluted with FC-2230, FC-2178 or FT-2481 for appropriate crosslink density. |
| FG-5690Q |
l
|
65.9 | 1.80 | 90 | -18 | 2220 | 205 | 955 | 76 | 10 | |
| Fabric Composite/Calendered Sheet Applications | |||||||||||
| FC-2120 |
l
|
65.9 | 1.80 | 23 | -18 | 2140 | 200 | 850 | 75 | 16 | Dipolymer for difficult extrusions. |
| FT-2350 |
l
|
68.6 | 1.86 | 56 | -14 | 2210 | 310 | 540 | 75 | 36 | Improved retention of elongation after long-term heat aging. Improved chemical and resistance over dipolymers. |
Non-Incorporated Cure Polymers
| Aggressive Oil/Coolant/Base Resistant Applications | |||||||||||
| Fluorel llTM Fluoroelastomer Products | |||||||||||
| * Incorporated cure | |||||||||||
| FX-11900* |
l
|
59.0 | 1.60 | 32 | -14 | 2270 | 220 | 850 | 74 | 43 | Excellent processability. Good metal adhesion. |
| Aflas TFE Elastomer Products(Press cure 10 min @177℃, Post cure 16 hrs @200℃ ) | |||||||||||
| FA-150L |
lV
|
57.0 | 1.55 | 35* | +2 | 1610 | 350 | 425 | 70 | 42 | Tank lining;viscosity modifier for other Aflas TFE Elastomer grades. |
| FA-150E |
lV
|
57.0 | 1.55 | 60* | +2 | 1905 | 370 | 390 | 70 | 48 | High speed extrusions. Improved flow for calender and grades. |
| FA-150P |
lV
|
57.0 | 1.55 | 95* | +2 | 2335 | 350 | 435 | 71 | 44 | General purpose grade for calendering, molding and extrusions. |
| FA-100S |
lV
|
57.0 | 1.55 | 160* | +3 | 2965 | 330 | 480 | 71 | 44 | Compresion molded O-rings, seals. Best overall physical properties. |
| FA-100H |
lV
|
57.0 | 1.55 | 110* | +3 | 2755 | 375 | 405 | 71 | 50 | Compression molded goods in demanding enviornments(i.e. oilfield). Best resistance to gas blistering and extrusion under high differential pressures. |
| Raw Gums/Peroxide Cure Grades | |||||||||||
| Raw Gums | |||||||||||
| FC-2211 |
ll
|
65.9 | 1.80 | 14 | -18 | 1870 | 180 | 600 | 75 | 17 | Blend with incorporated cure grades to lower viscosity and improve flow;coatings |
| FC-2145 |
ll
|
65.9 | 1.80 | 28 | -18 | 175 | 184 | 805 | 75 | 21 | Blend with incorporated cure grades to lower viscosity and improve flow. |
| FC-2230 |
ll
|
65.9 | 1.80 | 38 | -18 | 1995 | 165 | 972 | 73 | 15 | Blend with incorporated cure grades for processing or property modification. |
| FC-2178 |
ll
|
65.9 | 1.80 | 120 | -18 | 2275 | 177 | 1065 | 74 | 10 | Blend with incorporated cure grades to increase viscosity and green strength. |
| FC-2261Q |
ll
|
65.9 | 1.80 | 60 | -18 | 1870 | 240 | 630 | 77 | 14 | Blend with incorporated cure grades to increase viscosity and green strength. |
| FC-2430 |
ll
|
65.9 | 1.80 | 30 | -14 | 1950 | 255 | 340 | 74 | 38 | Improved elongation retention after iong-term heat aging. Improved acid and organic solvent resistance.Blends with incorporated cure gums; coatings. |
| FC-2481 |
ll
|
65.9 | 1.80 | 85 | -14 | 2200 | 220 | 799 | 75 | 24 | Improved elongation retention after iong-term heat aging. Improved acid and organic solvent resistance.Blends with incorporated cure gums; coatings. |
| Peroxide Cure Grades | |||||||||||
| FC-2260 |
lll
|
65.9 | 1.80 | 60 | -18 | 2345 | 225 | 745 | 76 | 25 | Peroxide curable gum for covulcanizable blends with other elastomer. |
| FLS-2650 |
lll
|
70.3 | 1.89 | 50 | -7 | 2600 | 230 | 780 | 72 | 28 | Peroxide curable high fluorine gum with low swell in aggressive fluids. |
| Test Compounds | ||||
| | | || | ||| | |V | |
| Polymer | 100 | 100 | 100 | 100 |
| Phosphonium Accelerator | 0.5 | |||
| Dihydroxy Crosslinker | 2.0 | |||
| MT Black(N990) | 30 | 30 | 30 | 30 |
| Mgo(mgo150,mgo-D) | 3 | 3 | 3 | |
| Ca(OH)2HP | 6 | 6 | ||
| Luperco™101XL Peroxide | 2.5 | |||
| Triallyl isocyanurate (TAIC) | 2.5 | 5 | ||
| Luperox F | 1 | |||
| Sodium Stearate | 1 | |||